dc.contributor.advisorMedina Calderón, Katia Luz
dc.contributor.authorQuispe Ampuero, Johana Milagro
dc.date.accessioned2015-08-13T13:48:44Z
dc.date.available2015-08-13T13:48:44Z
dc.date.issued2015
dc.identifier.urihttps://hdl.handle.net/20.500.12672/4318
dc.description.abstractEl objetivo de este estudio fue determinar la influencia del grabado ácido en la resistencia a la compresión del ionómero de vidrio base convencional (Ketac Bond) e híbrido (Vitrebond). Se elaboraron 40 probetas de 5mm de diámetro por 10mm de altura en un molde de plástico; divididas en dos grupos según el tipo de ionómero de vidrio base que su vez se subdividió en dos grupos según el grabado ácido. La preparación del ionómero se realizó bajo las indicaciones del fabricante. El grabado ácido se realizó con ácido fosfórico en gel al 37%, por 15 segundos, en la superficie superior de la probeta de ionómero, luego se procedió al lavado con agua destilada por 20 segundos y después se secó la superficie con papel toalla. Posteriormente, se calibraron las medidas de las probetas con un vernier y se comprobó el paralelismo de sus superficies, para luego ser almacenadas por 24 horas en una estufa a 37⁰ C hasta el momento de la prueba, la que se realizó en la máquina de ensayo universal (marca J. AMSLER). Los resultados obtenidos de la resistencia a la compresión promedio para cada grupo fue: ionómero de vidrio base convencional con grabado ácido fue 27.22 MPa, ionómero de vidrio base convencional sin grabado ácido fue 31.51 MPa, ionómero de vidrio base híbrido con grabado ácido fue 72.46 MPa y el ionómero de vidrio híbrido sin grabado ácido tuvo 95.54 MPa. Los resultados se analizaron mediante la prueba ANOVA de dos vías y para las comparaciones entre grupos se utilizó la prueba T Student. Se concluyó que el grabado ácido y el tipo de ionómero de vidrio influyen en la resistencia a la compresión.es
dc.description.abstractThe aim of this study was to determine the influence of acid etching on the compressive strength of convencional glass ionomer base (Ketac Bond) and hybrid glass ionomer base (Vitrebond). 40 specimens were elaborated of 5 mm in diameter by 10 mm in height and they were prepared in a plastic mold; divided into two groups according to the type of glass ionomer base and also, subdivided into two groups according to the etching. The preparation of the ionomer was performed under the manufacturer. The acid etching was performed with phosphoric acid 37%, for 15 seconds, on the upper surface of the specimen, then he proceeded to washing with distilled water for 20 seconds and then the surface wiped with paper towel. Subsequently, measures of the specimens were calibrated with a vernier and parallelism of the surfaces was found, and then be stored for 24 hours in an oven at 37⁰ C until the time of the test, which took place in the universal testing machine (Mark J. AMSLER). The results of resistance average compression for each group was: conventional glass ionomer base with acid etching was 27.22 MPa, conventional glass ionomer base without acid etching was 31.51 MPa, hybrid glass ionomer base with acid etching was 72.46 MPa and hybrid glass ionomer without acid etching was 95.54 MPa. The results were analyzed by two-way ANOVA and comparisons between groups, the Student t test was used. It was concluded that etching and glass ionomer type influence on the compressive strength. Keywords: Compressive strength, conventional glass ionomer base, hybrid glass ionomer base, acid etching.en
dc.description.uriTesises
dc.language.isospaes
dc.publisherUniversidad Nacional Mayor de San Marcoses
dc.rightsinfo:eu-repo/semantics/openAccesses
dc.sourceRepositorio de Tesis - UNMSMes
dc.sourceUniversidad Nacional Mayor de San Marcoses
dc.subjectResistencia a la compresiónes
dc.subjectIonómero de vidrio base convencionales
dc.subjectIonómero de vidrio base híbridoes
dc.subjectGrabado ácidoes
dc.titleInfluencia del grabado ácido en la resistencia a la compresión del ionómero de vidrio base convencional e híbridoes
dc.typeinfo:eu-repo/semantics/bachelorThesises